Bus Bar and Solids

 

We manufacture our superior range of bus bars &profiles that serve various purposes in diversified fields including power generation, transmission & distribution. We manufacture bars & profiles in all standard shapes and sizes and we also offer customization facility.
Today, we have been able to cater to the requirement of a large number of industries including:

  • Electrical industry
  • Energy transmission
  • Power generation
  • Telecommunication
  • Medical
  • Transportation
  • Automotive industries


Electrolytic tough pitch copper Bus Bar, Rods and Sections

Copper = 99.9% and Oxygen = 0.02% to 0.05%. ETP has a minimum conductivity rating of 99.5% IACS in annealed condition and 97% IACS in drawn condition.
 

SHERA make high conductivity copper Bus Bar, Rods and Sections

SHERA manufactures its own high purity high conductivity copper. Copper = 99.99%. It achieves a minimum of 101% IACS conductivity rating

Products

  • Bus BarBus Bar
  • Copper Bus Bar ProfilesCopper Bus Bar Profiles
  • Bus Bar SectionBus Bar Section
  • Bus Bar StripsBus Bar Strips
  • Tin Plated Bus BarTin Plated Bus Bar
  • Tin Plated Bus BarTin Plated Bus Bar
  • Round and Square BarRound and Square Bar
  • Copper RodCopper Rod

'SHERA' make ETP Copper Rod

  • Shera Copper ProductionShera Copper Production
  • Shera CoilShera Coil

Copper Solids Properties table

Alloy name Specifications Purity Oxygen Content   Temper Width Tensile Strength % elongation Hardness Bend Test Conductivity
  ASTM IS BS EN JIS    
Both having same physical properties
  over Upto & incl. Mpa (min)   HV Degree
(min)
% IACS
(min)
C-11000    (Cu-ETP) ASTM B187 IS:613 BS EN 13601 JIS H3140 99.90% 200 - 500
ppm
Annealed 6 mm and above 195 to 255 25 Max 60 180 99.25
Half Hard 6 mm 12 mm 250 20 70 to 90 120 97
    (Cu- SHERA)         99.99% 50 - 200
ppm
12 mm and above 230 20 70 to 90 120 97
        Full Hard 6 mm 90 mm 260 to 345 15 Min 90 120 97
        90 mm and above 230 to 345 15 Min 90 120 97

Aluminium Solid Properties table

CC grade Aluminium Bus Bar, tubes and sections

Alloy name
Specifications
Purity Temper Tensile Strength % Elongation Bend Test Electrical Conductivity
at 20 deg C
 
ASTM
IS
BS EN
JIS
    Mpa (min)  
Degree
(min)
% IACS (min)
CC grade
Aluminium
19501
 ASTM B236-07  IS:5082/1998
BS EN 755/2008
H4040 99.75
(min)
Annealed (O)
60
25
120
60
Half Hard (H1)
85
10
120
60
Full Hard (H2)
95
6
120
60

Size Range

  • Tin-plated copper busbars are manufactured as per International Standards such as JIS, DIN, BS and ASTM.
  • Process: In-house tin-plating controlled by computerized system
  • The Purity of Coating Material: Tin anode, 99.5% up
  • Coating Thickness: 3, 5 or 10 microns and as per customer’s requirement upto 50 microns